Mater.Phys.Mech.(MPM)
No 1, Vol. 25, 2016, pages 37-41

PREPARATION AND CHARACTERISTICS HEAT-RESISTANT COMPOSITES
WITH HIGH SPECIFIC STRENGTH DEVELOPING

М.I. Каrpov, V.P. Коrzhov, D.V. Prokhorov

Abstract

The work is devoted to the study of preparation and characteristics of the development of high-resistance composites with high specific strength. The basis for these composites is the system Nb-Al. For the preparation of the samples were applied powder metallurgy technology and the creation of laminated structures by combining diffusion bonding and batch rolling. Results showed that the most significant changes are noted due to an increase of the volume fraction of intermetallic phases, which provide high strength at high temperatures. Short-term three-point bending strength at 1300 °C reached 800 MPa. Also tests have been carry out for the creep at high temperature in a similar way.

Keywords: heat-resistant composites; high specific strength; diffusion bonding; batch rolling.

full paper (pdf, 1328 Kb)

ПОЛУЧЕНИЕ И ОСОБЕННОСТИ РАЗРАБОТКИ ЖАРОПРОЧНЫХ
КОМПОЗИТОВ С ВЫСОКОЙ УДЕЛЬНОЙ ПРОЧНОСТЬЮ

М.И. Карпов, В.П. Коржов, Д.В. Прохоров

Аннотация

В работе рассмотрены вопросы получения и особенности разработки жаропрочных композитов с высокой удельной прочностью, основой которых служит система Nb-Al. Для приготовления образцов применялись технологии порошковой металлургии и создания слоистых структур методом комбинирования диффузионной сварки и пакетной прокатки. Результаты показали, что самые значительные изменения отмечены за счет увеличения объемной доли интерметаллидных фаз, которые обеспечивают высокую прочность при высоких температурах. Кратковременная прочность на трехточечный изгиб при 1300 °С достигала 800 МПа. Кроме того, по аналогичной схеме были проведены испытания на длительную прочность при высоких температурах.

Ключевые слова: жаропрочные композиты; высокая удельная прочность; диффузионная сварка; пакетная прокатка.