The changes in grain boundary misorientations during plastic deformation of
titanium were studied by means of the EBSD technique. The misorientation of all types of the
grain boundaries including low- and high-angle boundaries, coincident site lattice (twin) and
arbitrary boundaries, deformation-induced boundaries and the boundaries of the original grains
was found to change during deformation. It was shown that the deformation may result in either
increasing or lowering of the boundaries misorientation and different segments of the same
grain boundary may develop principally differently. The most significant changes of the
boundary misorientation were found to be associated with the boundary junctions. The change
in misorientations during deformation was discussed interms of the interaction of a boundary
with dislocations and/or with other boundaries.
Keywords: metallic materials; plastic deformation; misorientations of grain boundaries. |
full paper (pdf, 1536 Kb)
|
Изменения в разориентации разных типов границ, включая мало- и
высокоугловые, двойниковые и произвольные, в том числе исходных и
деформационного происхождения были изучены при пластической деформации титана
и аустенитной нержавеющей стали с использованием EBSD анализа. Показано, что
деформация может приводить, как к росту, так и снижению разориентировки границ, а
различные сегменты тех же самых границ могут изменять разориентировку по-разному.
Наибольшие изменения в разориентировке были наблюдаемы в тройных стыках.
Изменение в разориентировке в ходе деформации обсуждается как результат
взаимодействия границ с дислокациями и/или с другими границами.
Ключевые слова: металлические материалы; пластическая деформация; разориентировки границ зерен. |
full paper (pdf, 1536 Kb)