MECHANICAL TESTING OF CFRP WITH EPOXY MATRIX

V.A. Yudin, V.I. Ivlev, N.E. Fomin, A.F. Sigachyov

Abstract

The results of tensile test samples of composite material based on epoxy resin content of carbon fabric, including the cyclic change of stress until the destruction of the sample. Defines the limits of strength, the effective elastic modulus, hysteresis loss. It was shown that the dependence of the module against mechanical stresses determined by the matrix, whereas the numerical value of the strength characteristics mostly depend on the filler. Mechanical cycling leads to a stabilization of the deformation characteristics of the material.

Keywords: epoxy resin; carbon; creep; mechanical properties; deformation.

full paper (pdf, 1648 Kb)

МЕХАНИЧЕСКИЕ ИСПЫТАНИЯ УГЛЕПЛАСТИКА С ЭПОКСИДНОЙ МАТРИЦЕЙ

В.А. Юдин, В.И. Ивлев, Н.Е. Фомин, А.Ф. Сигачев

Аннотация

В работе представлены результаты испытаний на растяжение образцов композитного материала на основе эпоксидной смолы с наполнением из углеткани, в том числе при циклическом изменении напряжения вплоть до разрушения образца. Определялись предел прочности, условный модуль упругости, потери на гистерезис. Показано, что характер зависимости модуля от механического напряжения определяется матрицей, тогда как численные значения прочностных характеристик зависят в основном от наполнителя. Зависимость потерь на гистерезис при механическом циклировании композита от числа циклов качественно одинакова с аналогичной зависимостью для чистой смолы

Ключевые слова: эпоксидная смола; карбон; ползучесть; механические свойства; деформация.

full paper (pdf, 1648 Kb)