The effect of pressure welding involving a shear strain along the contact surface on
the formation of a solid-state joint of dispersion-strengthened Ni-based superalloys EK79 and
EP975 is studied. Quality of the joints is assessed in terms of porosity and tensile strength tests.
It is shown that a 20 µm width transition diffusion zone is formed in the solid-state joint area
during the pressure welding process. EDX analysis revealed the occurrence of cross diffusion
processes of alloying elements W, Al, Cr in the diffusion zone. According to the tensile tests at
room temperature, it is found that the solid-state joint strength is about 0.49-0.62 of the EK79
alloy strength level.
Keywords: heat-resistant Ni-based superalloys, pressure welding, solid-state joint, heat treatment, shear strain, joint strength. |
full paper (pdf, 1872 Kb)
|
Исследовано влияние метода сварки давлением, включающего сдвиговую
компоненту деформации по контактной поверхности, на формирование твердофазного
соединения из дисперсионно-твердеющих никелевых сплавов ЭК79 и ЭП975, а также
проведена оценка его качества по пористости и прочности на отрыв. Показано, что в
процессе сварки давлением образуется переходная диффузионная зона шириной около
20 мкм. Методом энергодисперсионного микрорентгеноспектрального анализа
обнаружено, что в этой диффузионной зоне имеет место протекание процессов
встречной диффузии легирующих элементов, таких как W, Al, Cr и Fe. По результатам
испытаний на растяжение при комнатной температуре выявлено, что прочность
твердофазного соединения составляет 0.49-0.62 от прочности сплава ЭК79.
Ключевые слова: жаропрочные никелевые сплавы, сварка давлением, твердофазное соединение, термическая обработка, сдвиговая деформация, прочность соединения. |