The rare earth SmFe2 and CeFe2 Laves phases and solutions on base of them with
partial substitution by terbium ((Sm,Tb)Fe2, (Ce,Tb)Fe2) were obtained.
The lattice
parameters of compounds were refined by Rietveld method. To study the effect of substitution
on the magnitudes of magnetostriction and magnetization of alloys, measurements in the
temperature range 78-360 K in magnetic fields up to 1.2 T were carried out. Using Belov-Arrot
method, the Curie temperatures for series of compounds in Ce1-xTbxFe2 (x = 0; 0.1 and
0.2) system were determined. It was found that in the Sm1-xTbxFe2
system, a change in the
sign of magnetostriction should be observed at x = 0.4 - 0.45, which correlates well with
X-ray diffraction data.
Keywords: rare-earth intermetallic compounds, Laves phases, magnetostriction, magnetization, phase transition, CeFe2, SmFe2 |
full paper (pdf, 2272 Kb)
|
В работе получены редкоземельные фазы Лавеса SmFe2 и CeFe2 и системы
на их основе с частичным замещением тербием (Sm,Tb)Fe2 и (Ce,Tb)Fe2. С
использованием метода Ритвельда уточнены параметры решетки соединений,
проведены эксперименты по изучению влияния замещения на магнитострикцию и
намагниченность сплавов в интервале температур 78-360 К в магнитных полях до 1.2 Т.
Методом Белова-Аррота определены температуры Кюри соединений системы
Ce1-х,TbхFe2 (х = 0, 0.1 и 0.2).
Установлено, что в системе Sm1-xTbxFe2 смена знака
магнитострикции должна наблюдаться при х = 0.4 - 0.45, что хорошо коррелирует с
данными рентгеновской дифракции.
Ключевые слова: Редкоземельные интерметаллиды, фазы Лавеса, магнитострикция, намагниченность, фазовый переход, CeFe2, SmFe2 |