CORRELATION BETWEEN THE PRECURSOR DISPERSITY AND MECHANICAL
STRENGTH OF SOLID ELECTROLYTES BASED ON Ce2O3-ZrO2 SYSTEM

V.G. Konakov, S.N. Golubev, E.N. Solovyeva, I.Yu. Archakov, N.V. Borisova, A.V. Shorokhov

Abstract

Precursor powders with the final 9Се2O3-91ZrO2 (mol.%) composition were synthesized using the reverse precipitation sol-gel method varying the concentrations of the solutions of the initial salt reagents. A set of physical and chemical investigation approaches shows that the mechanical strength of Ce-Zr ceramics depends both on precursor dispersity and on CeO2 content.

Keywords: nanoceramics; precursor powders; dispersity; sol-gel synthesis; solid electrolytes; mechanical strength

full paper (pdf, 3728 Kb)

ВЗАИМОСВЯЗЬ ДИСПЕРСИОННОГО СОСТАВА ПРЕКУРСОРОВ И МЕХАНИЧЕСКОЙ
ПРОЧНОСТИ ТВЕРДЫХ ЭЛЕКТРОЛИТОВ НА ОСНОВЕ СИСТЕМЫ Ce2O3-ZrO2

В.Г. Конаков, С.Н. Голубев, Е.Н. Соловьева, И.Ю. Арчаков, Н.В. Борисова, А.В. Шорохов

Аннотация

Золь-гель методом в варианте обратного соосаждения путем варьирования концентраций растворов исходных солей-реагентов синтезированы порошки-прекурсоры итогового состава 9Се2O3-91ZrO2 (мол.%) с различным средним размером агломератов. С помощью комплекса физико-химических методов исследования показано, что механическая прочность Ce-Zr керамики зависит не только от дисперсности прекурсоров, но и от относительного содержания в них церия в виде CeO2.

Ключевые слова: нанокерамика, порошки-прекурсоры; дисперсность; золь-гель синтез; твердые электролиты; механическая прочность