NON-TRIVIAL CHANGES IN PHYSICAL AND MECHANICAL PROPERTIES AND
STRUCTURE OF LOW CARBON STEEL WIRE, PRODUCED BY ROLLING WITH
SHEAR AND COLD DRAWING

E.G. Pashinskaya, A.V. Zavdoveev, L.S. Metlov,
Y.I. Nepochatikh, A.A. Maksakova, V.M. Tkachenko

Abstract

The hereditary influence of the initial wire rod structure on the structure and physical-mechanical properties of the steel wire 08G2S, manufactured by rolling with shear, combined with the cold drawing is investigated. For comparison, the structure and properties of samples of the same steel wire, produced by commercial technology of rolling and drawing, were investigated. It has been shown that formation of the special structural state of low carbon steel by rolling with shear provides the increasing of the ductility and electric conductivity of wire in combination with satisfactory technological plasticity.

Keywords: rolling with shear; low-carbon steel; structure; resistivity; properties.

full paper (pdf, 2048 Kb)

НЕТРИВИАЛЬНЫЕ ИЗМЕНЕНИЯ ФИЗИКО-МЕХАНИЧЕСКИХ СВОЙСТВ И
СТРУКТУРЫ МАЛОУГЛЕРОДИСТОЙ ПРОВОЛОКИ, ПОЛУЧЕННОЙ
ПРОКАТКОЙ СО СДВИГОМ И ХОЛОДНЫМ ВОЛОЧЕНИЕМ

Е.Г. Пашинская, А.В. Завдовеев, Л.С. Метлов,
Ю.И. Непочатых, А.А. Максакова, В.М. Ткаченко

Аннотация

Исследовано наследственное влияние структуры катанки на физико- механические свойства проволоки из стали 08Г2С, изготовленной по технологии прокатки со сдвигом, совмещенной с холодным волочением. Для сравнения исследовались образцы, полученные с помощью стандартной технологии прокатки и волочения. Показано, что вследствие прокатки со сдвигом и волочения в проволоке формируется особое структурное состояние, которое приводит к повышению прочности и проводимости проволоки при удовлетворительной технологической пластичности.

Ключевые слова: прокатка со сдвигом; малоуглеродистая сталь; структура; сопротивление; свойства.