The paper presents the results of experimental studies of mechanical properties of ultrafine-grained
aluminum with a grain size of 700±200 nm resulting from the intensive plastic deformation by torsion of technical aluminum AD1 in combination with different modes of heat treatment. It is shown that microhardness and tensile strength of fine-grained material exceed the values of microhardness and tensile strength of the material as supplied more than two times and the elongation is reduced more than twice. It is noted that various modes of annealing after the intensive plastic deformation by torsion can lead to embrittlement of the material and increase its ductility.
Keywords: ultrafine-grained aluminium; heat treatment; microhardness; tensile strength. |
full paper (pdf, 3152 Kb)
|
В работе представлены результаты экспериментальных исследований механических свойств
ультрамелкозернистого, с размером зерна 700±200 нм, алюминия, полученного в результате интенсивной пластической деформации кручением (ИПДК) технического алюминия АД1 в комбинации с различными режимами термообработки. Показано, что микротвердость и прочность на разрыв ультрамелкозернистого материала превышают значения микротвердости и прочности на разрыв материала в состоянии поставки более чем в два раза, а относительное удлинение снижается более чем в два раза. При этом отмечается, что различные режимы отжига после ИПДК могут приводить как к охрупчиванию материала, так и повышению его пластичности.
Ключевые слова: ультрамелкозернистый алюминий; отжиг; микротвердость; прочность. |
full paper (pdf, 3152 Kb)